Kozik E.S., Koshelev S.I., Kushnarenko E.V., Scheinin B.M., Pravdin V.S., Solosin E.V. THE CORROSION RESISTANCE OF LOW-CARBON STEEL WITH GALVANIZED STEEL In the article investigated problems of increase the corrosion resistance low-carbon steel with galvanized steel. Found that for steel specimens diameter of 2–3 mm of the electrodes SSSI 13/55, MP-3, RLA-8 galvanically chrome-plated, nickel and cadmium after hydrogen sulfide native NACE test environment for 96 hours, followed by test notes on flexible bend corrosion resistance remained unchanged. Key words: mild steel, electroplating, galvanizing, cadmium-tion, chrome plating, corrosion testing, testing on flexible bend among NACE.
Kushnarenko V.M., Repyakh V.S., Chirkov E.Yu. THE ANALYSIS OF FAILURE CAUSES OF EQUIPMENT AND CONDUITS The authors examined the cases of the destruction of the equipment of bore holes, steel framework, conduits and components of conduits. They represented the basic reasons for the failures of equipment and conduits of the hydrogen sulfide-containing oil and gas condensate layers. Key words: equipment, demolition, plumbing, reason, fittings, tension.
Rezvykh V.A., Chirkov Yu.A., Kushnarenko E.V. TESTING METHODIC OF TUBE REAL EXAMPLES CONTACTING WITH SULPHURETTED HYDRIC MEDIUM Testing methodic of tube real examples contacting with sulphuretted hydric medium which allows to specify the influence of solid defect form on resistance to inner tube pressure and to compare with calculated meanings, is represented in this article.
2004,
|
|
Editor-in-chief |
Sergey Aleksandrovich MIROSHNIKOV |
|
|